Can anyone direct me to where I can find the X-Ray elastic constants for WC-Co or just WC?

06 January 2021 1 1K Report

I have searched all over the internet and I seem not to be arriving at its value. I need this value to perform some XRD measurements. Any help would be greatly appreciated.

Gerhard Martens

Dear Joseph Agyapong ,

you may have a look at:

https://onepetro.org/ISOPEIOPEC/proceedings-abstract/ISOPE93/All-ISOPE93/ISOPE-I-93-384/22467

Article A new model for evaluating the diffraction elastic constants of WC-Co

Try to get access via your institution

good luck

Badges
Science method

More Joseph Agyapong's questions See All

Installing Climate Data Operators?

Hello, I am trying to run Cygwin terminal but I experience a problem of cyproj-13.dll not found as below. I even checked on Cygwin but it is not there. Kindly help.

11 June 2024 4,502 0 View

How do I publish my research work here?

I need information on this question

21 May 2024 1,285 1 View

I design a unit cell metamatarial but the array structure does not behave like the unit cell, what could be the possible problem?

I created a unit cell in CST, and after that I created array from the structure, but my array structures do not behave like the unit cell, a have a DNG material in the unit cell and a SNG in the...

17 May 2024 4,700 6 View

Is there a glucose-free MEM-alpha medium commercially available?

For an assay I am planning to run I require a glucose-free MEM-alpha medium, I've seen papers where researchers state they use glucose-free MEM-alpha but they do not provide a supplier or catalog...

02 May 2024 4,004 0 View

IPSC to motor neurons?

Hi I have following questions regarding iPSC-derived motor neurons: 1. Is it possible to dettached mature motor neurons using accutase and reattach them on coated plates (matrigel, geltrx etc)?...

01 May 2024 3,047 0 View

Clarification on calculating LogID50?

Can someone please clarify the correct way to calculate LogID50 using the Reed and Muench method. Using the example values below: 10^-1 100% positive 10^-2 100% positive 10^-3 100% positive 10^-4...

01 May 2024 4,113 0 View

Does the alkyl chain between the carbonyl group and the C=C bond convert this group to saturated?

Find attached file

30 April 2024 6,886 0 View

What is the physical reason that hydroponic plants can be planted closer together then soil-based plants?

In other words, is it simply the nutrient supply that makes soil plants much less effective when they are closer together or does it have to do with the roots interfering with each other. If it's...

16 April 2024 6,718 4 View

Does the alkyl chain decrease the impact of the ring on C=O stretching IR?

Find the attached file.

15 April 2024 6,749 1 View

No cytokine or complement activation in my PBMC stimulation assay?

Hi I`m trying to detect immune response in vitro with my nanoparticle (virus-like particles) incorporating SARS-CoV-2 Spike protein. I inoculated quite a lot of nanoparticle in PBMC and inoculated...

09 April 2024 174 2 View

How to define an anisotropic material with asymmetric elastic compliance/stiffness matrix in ANSYS APDL?

I need to model an anisotropic material in which the Poisson's ratio ν_12 ≠ ν_21 and so on. Therefore, the elastic compliance matrix wouldn't be a symmetric one. In ANSYS APDL, for TB,ANEL...

09 August 2024 5,048 2 View

I need JCPDS file of LSFCO nanomaterial. Can anyone provide me?

Require for Rietveld refinement in XRD.

08 August 2024 3,081 2 View

How to understand this crystallographic phenomenon of low temperature crystals in zeolite?

During low-temperature testing, new diffraction peaks that appear could be indicative of several phenomena. In one of our tests, we observed notable new peaks around 40° and 45° in a specific...

06 August 2024 726 3 View

How to fix background error in rietveld refinement of one XRD peak using GSAS-II?

I want to refine one XRD peak of my in-situ xrd but the background is never working good which ultimately fails the refinement. How to refine and adjust the background using GSAS-II

05 August 2024 5,291 2 View

How to calculate the molar proportions of the oxides from the XRF analyses?

02 August 2024 2,565 2 View

Hello, regarding Mxene 2D titanium carbide?

I fabricated Ti3C2Tx using concentrated HF 40%, I plot an XRD as attached image below.. please let to know if I obtained it or not.

02 August 2024 6,789 4 View

Why Powder XRD is performed after cruhsing a crystal if Single Crystal XRD analysis of the same crystal has been performed already ?

What information we can get from PXRD analysis other than from SCXRD analysis of a crystal ?

30 July 2024 6,261 4 View

Can anyone guide me the best method to analyze the XRD data???

I will be doing an XRD on a sample which is powdered in natured and is a hydrogenated compound. I would like to know how we can understand the individual components and components by using the...

28 July 2024 4,548 2 View

Can we eliminate the stress singularity at the tip of the crack by manipulating the elastic constants?

The aim of the research here is to prevent the propagation of the crack in the fabricated elastic medium with useful applications.

25 July 2024 9,976 3 View

Guidance needed for preparing the hydrogel samples for the XRD instrument?

I'm working with a hydrogel sample and I'd like to perform XRD analysis. Can anyone offer guidance on preparing the hydrogel for the XRD instrument? Specifically, I'm unsure about the best method...

20 July 2024 3,611 4 View