Theoretically, at lower A/C excitation frequencies; say around 100 Hz, penetration of 5-10 mm is achievable in carbon steel (ferromagnetic) material. But, there is literature suggesting that this much depth is not achieved unless carbon steel is saturated by magnet. Any inputs?