Dear Mahdi,

CP-Titanium Grade2 is relatively soft and normally can be deformed easily by forging, rolling, rotary swaging or extrusion (depending of the shape you would like to have as semi-finished material). For a 20kg-Ingot you could start with hot deformation at approx. 850°C. The temperature can be reduced to 700°C in later deformation steps. For thin plates (sheet material) also room-temperature deformation is possible, but again that strongly depends of the degree of deformation you want to apply.

Kind regards

Carsten

Thank you dear Carsten Siemers