I think you should consider only the anode surface, because by anodic current density you control how much metal ions (for instance Al3+) will be released to solution.
For current density calculations you only consider the anode since that is where oxidation is taking place. The metal electrode (Fe or Al) is bi-polar hence consider the total surface area in solution.