The average crystallite size of nanocomposites was found from 25 nm to 44 nm. In addition, it was observed that the crystallite size of the M-phase decreased when the spinel phase increased. XRD analysis depicts the presence of both M and S phases in composites. The M-H loops analysis of SrFe12O19/NiFe2O4 composites indicates that the coercivity (3181–326 Oe), and saturation magnetization (57.5 Am2/kg. - 40 Am2/kg.) decreased when the spinel phase amount increased.Nanocomposites with weight ratios 9:1, 8:2, 7:3, 6:4 belong to a hard ferrite, while 5:5 shows soft magnetic nature. However, prepared composites possess a multi-domain structure.

https://doi.org/10.1016/j.jallcom.2021.163415