because of the metal quantity should be 30 to 65% solid in mentioned method. you must chose the hypoeutectic composition as main raw materials.In this method, Vortex method introduced as common procedure.
Hi, thanks alot for your attention, but i think you don't understand my question,i don't want to know semi solid processing.I want to know what method or methods is that i can add the powders in melt .but i made a mistake in expressing the question.
Production of Metal Matrix Composites by the Vortex Method and Investigation of the Effect of Changing Casting Temperature on Particles Ratio of Product-Composite
I think you have a lot of way to do it! but first of all, it is necessary to indicate your devices and or method of casting or semisolid casting!?? As mentioned in last answer Vortex method or Ultrasonic agitation or electromagnetic mixing could be helpful. Generally, the mechanical methods are clunky with shortcomings so it is better to choose your method from innovative process.