By what percentage ratio can we mix the water hyacinth stem and banyan root skin with mwcnt by using epoxy or PEEK resin?
Eldon Triggs
It will depend on the dispersion technique and any functionalization of the MWCNT. If you are dispersing the MWCNT in the epoxy by sonication or shear roll mixing before infusion into the fiber mat/cloth, then you should see percentages around 0.5 to 0.8wt%. You will need to look at any agglomeration problems as the wt% increases.
1 votes
1 thanks
David A Jesson
Will you be dispersing the mwcnt yourself? Or using a predispersed "masterbatch"?
1 votes
1 thanks