Is there any lowest possible level of dilution region above the interface by PTAW by controlling process parameters?

21 November 2015 1 3K Report

For base metal of 316 L SS and hard facing alloy of colmonoy, is there any lowest possible level of dilution region above the interface by PTAW by controlling process parameters? For Eg. 600 or 700 micron above the interface

Babu Bhaskaran

Refer this link:www.arcraftplasma.com/welding/PTWA.pdf

Refer this link:www.tandfonline.com/doi/pdf/10.1080/15560350802316744

Refer this link:iosrjournals.org/iosr-jmce/papers/ICAET-2014/me/volume.../17.pdf?...

Badges
Science topic

More Ramesh S's questions See All

Baseline drift in HPLC? What causes this?

Hello, Why do i see this baseline drift when i compare my blank (black) to the sample (blue)? Any suggestions as to why this happened? Thank you!

11 August 2024 3,770 4 View

How to increase simulation box size?

We intend to study the interaction between peptides and polymer (like PP, PE and PS) through MD simulations using Martini force fields ( Martini 2 for PP and Martini 3 for PE, PS). We have...

08 August 2024 4,842 0 View

How to prepare the nanoparticle treated fungal sample for Environmental SEM analysis?

A fungal strain was treated with nanoparticles. We want to do an environmental SEM analysis. So could anyone share your views on preparing the sample? Thank you.

07 August 2024 5,307 1 View

Absorption coefficient of methane?

Hello, Can anyone provide me with the absorption coefficient of methane gas at 7.7 um? Any reference?

06 August 2024 980 5 View

How are Large Models Exploring and Outputting Knowledge Understanding in Specific Content Areas, and What Does Academic Research Say About It?

Hello everyone！ I am currently exploring the performance of large models in understanding knowledge in specific domains, and attempting to construct a knowledge framework similar to what...

05 August 2024 5,729 2 View

Regarding a model for simulating battery charge and discharge, what do you consider to be high fidelity?

Regarding a model for simulating battery charge and discharge, what do you consider to be high fidelity? What is the acceptable percentage of error (regardless of the metric)? Could you suggest...

03 August 2024 5,358 0 View

How do i get an account to upload my published papers?

need to open an account to upload my published papers

01 August 2024 9,255 1 View

What is the problem with these tissue culture plants?

All plants are green but some of these plants becomes yellow. I did not found any reason. Please help me to find out the real problem.

01 August 2024 589 4 View

How to correctly use the UTE and ZTE pulse sequences in Bruker's ParaVision software?

I am using a Bruker 600M solid-state NMR spectrometer with a Micro 2.5 microimaging system. The test sample is a tube of 1M LiCl aqueous solution, and the nucleus detected is 1H. I am trying to...

01 August 2024 9,227 1 View

Is artifacts in XPS possible to build high deviation in binding energy larger than 5 eV??

Hello. Thanks for your consideration to see my question. Recently, I conducted XPS anaylsis of g-CN that is prepared from thermal polycondensation of DCDA, so-called conventional bulk-g-CN,...

30 July 2024 9,824 2 View

Is there a good macro photography kit for on-site metallurgical investigation?

I am looking to purchase a photography kit for onsite metallurgical investigations, such as capturing photos of worn areas, hot tears, cold tears etc. Could anyone suggest me a good...

22 July 2024 3,490 2 View

What could be the possible reason that sintering of polycrystalline diamond fabricated with tape casting has suddenly started failing?

I make polycrystalline diamond with tape casting followed by HPHT sintering. When i sintered the samples up till May, the sintering was good. When i sintered the samples in June and July at the...

16 July 2024 3,212 5 View

What binders suggestion that I can use for zinc alloy?

I am working on powder metallurgy, and during the compaction process, the powder does not pelletize and remains in its powder form. To address this issue, I am considering using binders to improve...

13 July 2024 9,003 2 View

What may cause whitish discolor of polycrystalline diamond surface, and cracks near edge?

I am preparing polycrystalline diamond (PCD) with tape casting. The powder is 8~12 um. After drying of tapes, I place several tapes in Ta cup without warm-pressing. Next, debinding is carried...

23 June 2024 7,758 2 View

How do we interpret the origin statement ?

Crystallography Doubt_International Table of Crystallography In the space-group number 185 of ITA (see Attachment), how do we interpret the origin statement?

08 May 2024 10,055 0 View

Why stainless steel is not attractive to magnetic feild?

In material science, steel have more group, So what is the best explain answer according in metallurgy science?

21 March 2024 835 4 View

Phase Grain Contiguity & Bonding Phase Thickness of Powder Composite?

Hi. Can anyone explain to me these terms: 1) Phase grain contiguity 2) Bonding phase thickness Q: Simple explanation on this? How to measure this properties? Software / formula ? How does this...

03 December 2023 4,823 1 View

What mechanical tests are important for magnesium scaffolds that have a high percentage of porosity and are produced by powder metallurgy?

What mechanical tests are important for magnesium scaffolds that have a high percentage of porosity and are produced by powder metallurgy? Does this include only compression tests? Can bending and...

21 October 2023 9,785 1 View

What viscosity Methyl cellulose binder is used for tape casting of 10 um powder particles? What are general recommendations for such sized particles?

I am using 4000 cP methyl cellulose for aqueous tape casting. Since it gives very viscous solution, I am dissolving it in 1.5 wt% in 98.5 wt% DI water. Still it is a very viscous solution. Because...

17 October 2023 1,919 2 View

What is the maximum Si content in Al-Si alloys and the parting limit during dealloying/chemical leaching?

We recently 3D printed (SLM) hypereutectic (high Si)% Al-Si-alloys and chemically removed the Al afterwards (via HCl (aq)) in order do get a porous structure, which worked quite well. 1.) I was...

16 October 2023 1,716 1 View