I synthesized my carbon quantum dots (CQDs) using a green synthesis method with deionized water as the solvent. During TEM imaging on a copper grid, my sample appears to melt or degrade under the electron beam. What could be the possible causes, and how can I prevent this issue? Any insights or recommendations would be greatly appreciated