How we can increase the printing speed of fused deposition modelling technology ?

Pulak Adhikary @Pulak-Adhikary

22 August 2023 1 3K Report

How the nozzle temperature can be increased without causing blockage or failure

Amit kalubhai Anakiya

There are a number of steps that you can try, as permitted by your model:

1. Reduce the infill percentage.

2. Increase the layer thickness.

3. Decrease the skirt size.

4. Generate an STL file in a way that allows multiple small components to be printed at once.

Badges
Science topic

Similar topics
Engineering
Modeling

More Pulak Adhikary's questions See All

After DOS calculation in material studio software, where can I found the fermi energy value?

I was not very familiar with material studio software. I have run the DOS calculation, but I can not find the Fermi energy in the DOS output file. I have to do the Fermi energy level correction...

20 April 2024 8,223 0 View

How can I optimize the problem regarding the radical interaction?

I am calculation for optimization of TS of an aromatic molecule and a hydroxyl radical. In this DFT calculation, I am using the functional B3lyp/6-311+G(d,p) in the Gaussian16. The charge and...

04 April 2024 8,499 1 View

What is the main problem here ?

It is comsol 6.1 .

29 January 2024 3,626 1 View

About Comsol Multiphysics , how can i active the legend section?

Greeting everyone. Here, I can face a problem. I need to activate the legend section, but I cannot do this. Please help me. How can I activate the legend section? Here is the attached related file...

24 January 2024 185 1 View

What is the main problem here ?

Hello, During the simulation in comsol multiphysics I am facing the following error. Can somebody suggest me how to resolve this error.

18 January 2024 7,995 3 View

For liquid liquid extraction of phenolic compound from water solution of phenol, which solvent should be best option?

I want to analyze degradation intermediates of phenolic compound through GC-MS analysis which I had carried out in aqueous solution. For liq-liq extraction of phenolic compound from aqueous...

25 December 2023 1,205 4 View

During calcination process of nanoparticle preparation crucible lid should be closed or open??

Specially for preparation metal oxide nanoparticles using co-precipitation method. If crucible is open, then there may be risk of contamination inside the muffle furnace. I want to clarify this point.

27 September 2023 5,264 2 View

Why both I.P and S.C injection of CT26 colon cancer cell line is unable to form colon cancer? can anyone suggest me the particular reason?

We wanted to create a syngeneic colon cancer mouse model for my research work. For this, I have chosen CT26 cells, a colon cancer cell line. Many literature reviews reported that the CT26 (1*106)...

20 August 2023 4,922 0 View

I am having trouble inducing colon cancer in Balb/c mice model using CT-26 cells. Can anyone suggest me any specific procedure?

Is there any specific procedure / protocol to immunosuppress the mice and then to induce colon cancer using CT-26 cells? Can anyone suggest any specific immunosuppressors that can be used for...

17 August 2023 5,990 0 View

Can we use tetrahedron method with Blöchl corrections for energy minimization of slab?

For the calculation of the total energy in VASP, it is recommended to use tetrahedron method with Blöchl corrections (ISMEAR=-5). And for 2D slabs in the z direction (perpendicular to the...

10 August 2023 6,615 2 View

What may be the reasons for failures of Tube toi Tube Sheet Joints in Boiler Drum ?

We have observed that tube to tube sheet joint leaked in our boiler and needs to overcome same by knowing the root cause.

08 August 2024 3,161 0 View

How to find a reaction is reversible or irreversible in CV? How to know the number of electrons transfer?

My screen printed electrode CV is given here. For Nerstean one electron reaction the delta E value should be close to 57 mV and ration of Ic/Ia should be close to 1. I did CV of my screen printed...

30 July 2024 4,671 3 View

Prevent sedimentation and maintain the suspension of powder particles in the resin ?

Hello, I am experiencing an issue with mixing micro powder with resin in a 3D printer. The problem is that sedimentation occurs after a short period (about half an hour to an hour). Could you...

23 July 2024 1,672 0 View

How to avoid background signal in screen printed electrode?

Hi, I am doing aptamer based electrochemical biosensor. First, I cleaned screen printed gold electrode using 0.5M H2SO4. Then, immobilized aptamer followed by blocking using 2mM MCH. I use...

06 July 2024 9,852 1 View

Zero pivot in Abaqus concrete 3D printing simulation using model change?

Recently I've been working on a simulation of concrete 3D printing, and has successfully simulated a layer-by-layer 3D printing process using model change. However, when I proceeded to try...

06 July 2024 2,130 0 View

Are there any people using biolegend anti- mouse CCR2-BV785?

Hi, I'm working on heart flow cytometry, and I use anti-mouse CCR2-BV785 (biolegend, cat150621) for staining, 20 minutes, 4 degree. But I couldn't see any CCR2+ cells. So I'm not sure if it's...

03 July 2024 3,969 4 View

Can SimaPro be used to simulate/analyse Biodegradation of Specimens?

I am looking at ways to investigate the biodegradation of 3D printed specimen as part of my research. To what extent can SimaPro be used to do this? The idea is to demonstrate the biodegradation...

02 July 2024 2,730 2 View

Abaqus 2023 - How to access element - scale for implementing a failure criteria with subroutines (UMAT, USDFLD, UEXTERNALDB, ..) ?

Hi all, I am working on subroutines (UMAT and others) with Abaqus. I would need to calculate the average stress by element to eventually change its Young modulus. How should I implement that...

25 June 2024 5,205 1 View

Abaqus 2023 - How to access element - scale for implementing a failure criteria with subroutines (UMAT, USDFLD, UEXTERNALDB, ..) ?

Hi all, Second question on the same or so topic. I am working on subroutines (UMAT and others) for Abaqus to implement Tsai-Wu failure criteria for non-composite structures (I work on long...

25 June 2024 2,955 1 View

How to do polishing for EBSD of Ti-6Al-4V alloy fabricating by 3d printing?

I am polishing with emery papers with different grit sizes followed by diamond polishing and colloidal sols after ultrasonication with no scratch After that when I go to EBSD CI is not coming....

25 June 2024 2,402 3 View