It really depends on what material, as different polymers have different tendencies for interchain interactions and therefore poly crystallite formation. Usually, a thin film is deposited from a polymer solution. The deposition morphology can be controlled to some extent by the characteristics of the substrate - e.g. crystallinity (mica, silicon, gold) or surface treatment (hydrophobicity, hydrophillicity, functionalisation).