My topic is to study the mechanical properties of Mg/Al2O3/Gr hybrid metal matrix composites by using powder metallurgy technique. I am using sintering temperature rang 400-550 oC. I am now encountering problem to form the samples which I meant that the samples disintegrate during sintering process even I tried to use PVA as a binder the same things happened. May you guide me to settle this issue.