I am trying to find normal stresses (in the global x-y-z direction) of individual layups (plies) in ABAQUS. While post processing I only find S11 S22 S12. Do I always have to use a transformation matrix to find my Sxx Syy and Sxy? Is there a GUI/ Command way to extract the stresses in each ply in xyz directions?
Thank you
Djamel Boutagouga
Hi, everyone.
in the visualization mode. you can create the coordinate system you need.
next, go to Result -> Options -> Transformation. chose "Userspecified"
and you choose the coordinate System you have created.
Also, you can choose the "Layup-orientation" option
0 votes
0 thanks