Consider to dry the hematite ore powder before sieve size analysis; that should also deagglomerate the dry powder. It seems adequate to regrind the oversize fraction by the same previous selected grinding/milling method (not disclosed in the enunciate), perhaps by about the same time, as it performed rather well, as much as I can understand from the query enunciate.