Depending on the pore size of your material you might look into mercury intrusion. This iwll allow you to analyze pores within the range 3.6 nm - 1.1 mm. More complex methods such as SAXS and NMR experiments can also be used.
T2 can be correlated to the pore size, hence, a T2 distribution can be correlated to the PSD. this method is still kind of new but many groups are working on it.