You can plot the real part of admittance (or real part of conductivity) against frequency.  For low frequencies you have a region nearly independent of frequency (the dc limit), the frequency where the curve starts to rise linearly is the critical frequency above which ac behavior sets in. Inverse of the critical frequency gives roughly the relaxation time. For higher frequencies, i.e. lower times the charge carriers do not 'see' the whole sample.