2000 g/mol very low molecular weight for the electrospining study. According to my experience, 80000 g/mol very suitable for electrospining and you can get smooth fibers or you can create a blend system with a higher molecular weight polymer and 2000 g/mol polycaprolactone.
This molecular weight is very low for Electrospining due to low viscosity so you can mixed with high molecular weight of commercial PCL higher as blend or core shell.