Hello,
I have been trying to calculate the melting temperature of a homogeneous alloy that is grown in non-equilibrium growth conditions during the ultra-fast annealing via an excimer laser ( bellow 100 ns pulse duration). is there a way or an equation to calculate it, and does it correlate to the weighted averages of the melting temperatures of pure elements constituting the alloy.
Thank you for your help.
Hi Salim,
It is better to use TTT-diagrams. An example is attached.
Hello Hassan,
Thank you for the prompt reply, However for this system, there is no TTT diagram available, so I am looking to for a model or a system of equations that would allow me to predict it.
Please specify the composition of the examined alloy. It's impossible to say something without use of both phase diagram and TTT diagram. The base of the weighted averages most probably will be incorrect.