I want to distinguish martensite and lower bainite in AISI 4340 low alloy steel microstructure. How can do it? please guide me. thank you?

you know, it's difficult to distinguish lower bainite and martensite in low alloy steel.

31 December 2018 8,897 5 View

What is a suitable solution for colour etch of AISI 4340 steel?

thank you

10 November 2017 7,751 0 View

What is a suitable solution for colour etch of AISI 4340 steel?

i want to seperate bainite and martensite microstructures in my metallography pictures. what is the best solution for it?

10 November 2017 549 1 View

What is a suitable solution for colour etch of AISI 4340 steel?

thank you.

08 September 2017 2,746 0 View

What is the production process of CaFe ferroalloys?

I looking for ferro calcium production process

03 March 2021 1,755 4 View

12% ledeburitic cold work tool steel, etched for revealing retained austenite, any help for clarifying?

Hello everyone. Given microstructure image belongs to a 12% ledeburitic cold work tool steel (annealed and tempered). The sample was etched with picral (100 mL ethanol and 4 g picric acid). I...

02 March 2021 4,119 3 View

Which is the most efficient etching solution for nickel based alloys?

Which solution reveals the microstructure and features of nickel-based alloys?

02 March 2021 2,221 3 View

Why Austenite grains in steel show much more twinning than ferrite grains?

It is oftentimes said to be a distinctive metallographic trait that differentiates a fully austenitic and a fully felly ferritic steel without etching that might distinguish between two. Why...

02 March 2021 728 2 View

How Can I bring as much common elements in steel as possible to calculate stable phase(s) in OpenCalphad?

As I was tweaking step-by-step OpenCalphad6 Macros step1.ocm involving phase and thermal property calculation of a High-speed steel, I could not incorporate more than 6 elements in the steel...

01 March 2021 8,840 1 View

I need to accelerate corrosion in steel parts that are used in a salt-water environment. Is there a technique for doing so?

I have a structure that employs d-ring swiveling tie-downs that corrode during use and become "frozen". I have sample swivel assemblies that I wish to corrode to see if I can free them using one...

01 March 2021 3,739 3 View

Why is my platinum counter electrode getting dirty during electrodeposition?

I am conducting anodic electrodeposition of MnO2 onto a stainless steel substrate, using a platinum strip as a counter electrode. This is done galvanostatically, with the current held between 5...

27 February 2021 1,829 3 View

How can I selectively dry etch Ti on a polymer substrate?

24 February 2021 5,378 1 View

What kind of steel moulds are used for hot pressing metal powders?

My main concern is that the metal powders should not weld to the mold surface and I should easily be able to eject out the pressed samples. I am looking for alternative for graphite moulds. The...

22 February 2021 2,965 4 View

What are effects of steel jacketing on flexural strength?

Dear all, If steel jacketing is used to retrofit a reinforced-concrete (RC) column, can we use it to improve flexural strength? I understand that we leave gaps between the ends of the jacket and...

22 February 2021 1,906 5 View