usually one calculates from their SQUID magnetometry MvT data
Ueff = 2.828*SQRT(Xp*T)
Where Ueff is the effective magnetic moment, Xp is the corrected paramagnetic susceptibility, and T is temperature
However do we need account for the Weiss constant also to get the correct result when considering ferro/antiferromagnetic materials?
so
Ueff = 2.828*SQRT(Xp*(T-weiss constant)