Does DMSO delaminate graphene or just peel it off from the substrate (SiO2)?

Can we classify HV and LV lines based on line length?

I have dataset which shows the length of power lines. I need to classify the lines based on the line length. Is there a rule to classify the High voltage (HV) and low voltage (LV) lines based on...

03 March 2021 4,116 4 View

Should we change media after1st 6hrs after plating HUVEC bought from INVITROGEN?it's not recomended by invitrogen.Will DMSO present in stock matter?

We have HUVEC bought from Invitrogen. Cat no -C-003-5c. while first plating the cells we have bought the protocol suggests not to centrifuge the cell with media to remove the DMSO. Should we...

02 March 2021 3,713 2 View

What are the new 2D nanomaterials were used for Silver nanoparticles stabilization?

In the stabilization of AgNPs are vital in current research interest. However, some of the 2D nano-materials like graphene oxide, MoS2, etc... previously used to stabilize it. But still they shown...

01 March 2021 2,207 3 View

Bought HUVEC from Invitrgen.need to revive it.expected it is cryofreezed in DMSO.Do I need to remove the DMSO for plating the cell for the 1st time?

After I cryofreeze the cell do I need to remove the DMSO for culturing the cell for next passages .

28 February 2021 7,738 3 View

POlymer+DMSO solution and moisture??

What could be the reason of moisture at the sides of Vial when I am preparing my polmyer+DMSO solution for membrane fabrication? What etiquettes I am possibly missing here?

28 February 2021 6,516 5 View

Can impedance of antenna be less than 50 ohms?

I am simulating helix antenna in hfss, right now, giving excitation with 50 ohms port. When I see the results of Z parameter (real). It shows lower than 50 ohms. Do not understand, if it can be...

27 February 2021 4,218 7 View

What condition required for coating of Fe3O4@SiO2 by using APTES?

I tried coating Fe3O4@ SiO2 by using APTES in 5% water-ethanol but it is not coated. Kindly suggest a solution for it. Thanks

24 February 2021 5,992 4 View

Thermal reduction of graphene oxide.?

I am trying to reduce graphene oxide by thermally but I have no proper information regarding this. Can any one help me regarding the details about temperature and time for the reduction of...

23 February 2021 4,155 4 View

Is there an ideal incubation time of RGO-modified SPCE before subsequent use, i.e., electrochemical characterization or further modification?

I notice that upon washing and air-drying of my RGO/SPCE surface and characterizing again via DPV, the current response towards ferricyanide probe significantly decreases. My worry is that the...

22 February 2021 5,324 3 View

How to dilute Toxin-DMSO solution?

I have a concentrated solution of a toxin(50 micromolar) in DMSO 100%. I need to dilute it inorder to dilute both the toxin and DMSO wich can be toxic to cells. Which would you guys recommend to...

19 February 2021 7,447 2 View

Thomas Pozegic

To answer the title, check the 2D peak using Raman spectroscopy whether you have a single layer graphene. If it is a single peak, you have a single layer, otherwise it is multi-layered.

Liu Beiyun

I have not used DMSO , but some reagents have strong surface tension on the graphene, which could damage the material. You can try to reduce the soaking time and avoid cleaning the graphene with deionized water.