We have prepared MoS2 but the delamination process has not worked very well, so the layers obtained are still too large. We have tried a chemical process and high power ultrasound treatment, but delamination is very slow. Could someone suggest an efficient process? We have followed some processes described in several papers but they do not work very well ...
Thanks!
Dear Francisco Manuel Marquez I assume that you already checked the following potentially useful article. If not, it might help you in your analysis:
Strongly luminescent monolayered MoS2 prepared by effective ultrasound exfoliation
Article Strongly luminescent monolayered MoS2 prepared by effective ...
The paper is freely available as public full text on RG. Also please have a look at the following potentially useful RG link:
Controlled Exfoliation of MoS2 Crystals into Trilayer Nanosheets
Article Controlled Exfoliation of MoS2 Crystals into Trilayer Nanosheets
Good luck with your experiments!
Thanks Frank!!
We have tried these processes, but delamination is very inefficient. Maybe (and that's what I think) the paper doesn't include all the details of the process ... but we'll keep trying.