Can anyone tell me calcination temperature of the basic alumina?

28 April 2016 1 3K Report

I want best temperature for calcination to achieve the neutral alumina

calcine the hydrated alumina(bayer alumina) at >1150° C and you can achive alpha alumina the stable phase of alumina .for densification high temperature sintering is required.

Badges
Science method

More Arezoo sh. dadkhah's questions See All

Drawing fullerene more than 60 carbon?

I have ChemDraw 22.2.0 and I want to draw PC70BM but I just found C60 and less in the templates so, any one can help me ?

18 June 2024 3,098 3 View

How to find out Laccase enzyme's activity other than using ABTS?

After purifying Laccase enzyme (Bacterial origin), I tried performing enzyme assay using ABTS which is a known substrate. Still I am unable to validate its activity using the said substrate....

21 January 2024 5,159 0 View

How long can PBMCs be stored at -70°C with good quality?

Can storing PBMCs at -70°C for a long time affect the population of PBMCs?

15 January 2024 8,010 3 View

Method of measuring sulfur for molybdenum oxide?

What is the method of measuring sulfur for minerals such as metal oxide or molybdenum oxide through Leco furnace (or similar furnaces) at different temperatures, times and weights after leaching...

11 November 2023 3,345 2 View

Why is my qPCR not working?

Hi y'all, I am running into some difficulties with qPCR (SYBR). To give y'all a brief background summary, I transfected some cells (ASO) and am running qPCR to see its effect on known genes using...

08 November 2023 9,775 6 View

Noticing a brown/bronze tint on my human fetal spinal cord sections after RNAscope - not sure what it is?

Dear all, I am running an RNAscope experiment on human fetal spinal cord sections, roughly gestational week 15. After running my latest round of experiments, I've noticed a brown/bronze tint on...

24 August 2023 3,876 0 View

A research question about the perpendiculars and the final solution?

Hey I would be happy to receive help and guidance on a research question about the nymphs and the final solution. Is the extermination of the Jews, the "Final Solution" part of the Nazi ideology?...

05 August 2023 1,157 3 View

What is the best cytotoxicity test for car-nk cell evaluation? (with protocol)?

cytotoxicity test

30 July 2023 1,006 1 View

Joint stiffness constant needed in this case?

Fig.1 in the attached files shows a typical case of the joint stiffness constant case. In this case, the external loads are applied to the plate, normally named as member. Normally the bolt load...

18 May 2023 6,428 0 View

What is the length of the couple region in the riblet coupler?

Hello I want to design a riblet hybrid coupler (Short Slot Hybrid Coupler) in X-band. 1- What should be the length of the couple region, the distance between the two common walls? 2- What...

17 March 2023 6,712 3 View

Need heterogeneous catalysts calcined before reduction?

Metal-containing heterogeneous catalysts often need to be calcined before reduction, so what are some examples of catalysts that perform better without calcination? What is the reason and how many...

05 August 2024 909 2 View

I have calcined my catalysts without flowing air from the compressed air cylinder will there be any problem with my reaction if i use that catalysts?

FYI Catalyst is MFI zeolite Si/Al = 140,25.40.11.5,15 I am using this catalyst to study methanol to DME conversion

25 July 2024 2,486 2 View

A twin-shaft kiln or a rotary kiln for lime production 1 class? if compressive strength of limestone is low 60 MPa?

My research work is related to the calcination of limestone. I have a complex question and would like to consult with experts in this field. Could you please advise which kiln to choose (a...

18 July 2024 1,390 2 View

How to calculate the proportions in grams or milliliters of the compounds for 60 mL of SAPO-11 zeolite precursor gel?

It is required to make a precursor gel for a SAPO-11 Zeolite, the compounds are the following: * As a source of Al: Aluminum Isopropoxide (98%) Formula: C9 H21 O3 Al PM: 204.24 g/mol Density:...

01 July 2024 617 3 View

How to decide mass scaling in ABAQUS?

I am doing orthogonal cutting of aluminum. My forces are changing according to mass scaling. How to decide the scaling factor?

01 July 2024 3,749 0 View

Can anyone help with a sample of Kraft pulp process lime mud (CaCO3)?

Can anyone help with a sample of Kraft pulp process lime mud (CaCO3) I need a sample of 250g to run R&D lab testing. I am based in the UK and I am struggling to get hold of some lime mud...

01 July 2024 9,217 0 View

How can repair crack in alumina to make it helium leak tight for ultra high vacuum application??

I want to close crack in alumina kindly suggest any glue or epoxy to close leak.

27 June 2024 10,110 1 View

Can I use an image of the same sample in two different publications?

I'm trying to submit a paper, but two different manuscripts are being prepared. One is by me and one is by a collaborator who is using my samples. I know it's unethical to reuse the same data in...

25 June 2024 6,110 2 View

Why my mesh convergence is failing in ABAQUS?

I am doing 2D orthogonal cutting simulation in ABAQUS for aluminum. Reducing mesh size up to 0.08 mm reduces the error to 3% but further reduction leads to increase in error from 3 to 39%. Why I...

23 June 2024 9,080 0 View

ABAQUS - Face could not be partitioned. How to resolve this error?

I am doing orthogonal machining of aluminum in 2D. However, when partitioning for depth of cut with a sketch on face strategy with a parting line, it says that face could not be partitioned. How...

18 June 2024 8,000 0 View