for example, Ag has its experimental optical peak at 3.2 eV. Now, at what eV/Hz do the Al and Cu have their optical peak? I am looking for any theoretical or, experimental calculation on that.
Your kind help will be very much appreciated
Thanking you in advance
Hi Shaikat
If you are talking about the plasmon peak for nanoparticles, it actually depends on the shape of the particles and, to some extent, on their size. It also depends in which medium they are.
For small (
Maybe could be usefull also this article http://dx.doi.org/10.1063/1.3552077
Dr. David Rioux, special thanks for your very helpful comment. It is very helpful. Thank you very much
Dr. Vladimir S. Myasnichenko and Dr. Massimo Ottonelli
Thank you very much for your helpful comments. It has been very helpful for me.
Thank you again for being very kind to me
Best Regards