Transparent conductive oxides intrinsically behave as metal like which means that they are as deposited as nondegenrate semiconductors with their Fermi level lying inside the band. The carrier concentration is high however the mobility is relatively low because of the fine grained polycrystalline nature. Because they are nondegenrate it is very hard to change their type by doping.