8 Questions 11 Answers 0 Followers
Questions related from Dinesh Saini
I have produced Cu added (Ni is replaced by Cu) NiMnSn alloys by ball milling method. After ice water quenching, a mixed phase microstructure (parent phase + martensite phase ) is obtained. Why...
25 October 2017 3,918 4 View
Hello researchers, I have prepared a Ni50Mn40Sn10 (atomic %) alloy by Arc melting technique. The obtained alloy was subjected to vacuum heat treatment at 950 degree celcius for 72 hrs followed by...
10 October 2017 8,449 2 View
Hello researchers, I have prepared a Ni50Mn40Sn10 alloy by Arc melting technique. The obtained alloy was subjected to vacuum heat treatment at 950 degree celcius for 72 hrs followed by ice water...
30 August 2017 1,468 1 View
Dear Researchers, I have prepared some alloy samples (NiCuMnSn) by ball milling. The obtained powder was converted into 10mm pellets and then heat treated at 950 degree celcius (under very high...
29 September 2016 7,010 1 View
I am working with NiMnSn heusler alloys. I have produced powder samples by ball milling technique. The obtained powder was compacted to make pellet and sintering was done. Now I want to know, can...
29 January 2016 3,657 4 View
hello guys My question is "how to determine lattice parameter of a tetragonal system by using Nelson -Riley equation"....?
23 September 2015 6,980 0 View
If I do the ball milling of Ni50Mn45Sn5 (atomic %) for 20 hours in presence of Toluene as process controlling agent. Argon flow and vacuum were not maintained during milling. (i) Will the outcome...
31 March 2015 7,972 2 View
I have an alloy sample and the selected area diffraction pattern of this alloy is showing polycrystalline rings. How do I calculate planes from those rings?
17 March 2015 6,726 3 View