In raman the intensity not only depends on the material but also in the parameters os the experiment, laser, power, focus, etc. So is not that easy to do this comparison.
If you using the same parameters to measure both samples, then the Raman signal would be proportional to the material quantity. If the exfoliated graphite is only a few layers then the signal from the bulk sample should be larger.