Dear Mohammad,

You can use, of course, Pauling's rules, they will give you readily the answer you want. Another perspective, perhaps more intuitive, is the following: if silicate tetrahedra share faces, you cannot construct a crystal (3D repetition of a motif). I hope I could help you.