Although not a book, I believe that the paper "Rietveld refinement guidelines" from McCusker et al. is an excellent work on the general guidelines for Rietveld refinement analysis.
Although not a book, I believe that the paper "Rietveld refinement guidelines" from McCusker et al. is an excellent work on the general guidelines for Rietveld refinement analysis.
I suggest these books, because crystallographic data refinement is very tricky business. Since fitting procedure involves numerous variables, it is possible to fit almost anything perfectly without a problem. However, there is a big question: does these refined parameters of the structure make sense (both chemically and physically)?
If you do not make your basic understanding clear in the beginning, you will put yourself in a potential high risk of making a big mistakes in the future. These books will give you a quite detail information regarding diffraction, structural characterization and the Rietveld refinement.