Pierluigi Traverso

Dear Dr. Pierluigi Traverso,

Thank you very much for your answer.

Very sorry that I didn't describe my issue clearly.

I used the PMMA: curing agent=10:1, do I need to increase or decrease this value based on my experiment that I have modified again?

Thank you and best regards

We use Omnicoat (from MIcrochem) as a layer to lift of polymer membranes.

E.g. see:

Article Conformable optical coatings with epsilon near zero response

or

Article Flexible patches for mm-wave holography

Dear Shiru,

we use metallic sacrifical layers to obtain polymer films. They can be dissolved in acids or electrochemical with anodic dissolving.

Good luck and greetings Folke