If we quench a Fe-SMA with different compositions of brine solution, what will be the on the phase transformation temperatures of the alloy? How brine solution composition affects the quenching effect of brine solution?
phase transformation depends purely on quenching rate, phase transformation temperature depends on composition of the material
Especially - in a single base quenching medium, we may not expect a big difference in phase transformation characteristics
all you can do is,
1. try for existing research - That is what you did a post here, i also look in to this question for any response from researchers - it looks combination of material and medium of quenching - people may not worked - that is why no reply, i google, it looks like different quenching medium results are coming
Article Structure-Property Relationship of Cu-Al-Ni-Fe Shape Memory ...
2. So, better to go with you own research experimentation
Thank you very much S. Gunabalan for your help. I have gone through literature and the above mentioned article is part of my literature review. in this article, brine of only one composition is used whie I want to know about quenching with multiple compositions of brine solutions. So, I will try own experimentation. Thanks again for your suggestion.