I agree qith Jeremy. Without seeing the spectra however I would say that you are talking about the bandgap absorption (~190 nm in bulk YAG) and any kind of possible defect absorption in the Vis. The defects would be related to e.g. strain resulting from nano-effects, could be contaminants etc. Seeing spectra would help, also other data.