Hi,
So, I have experimental data from DMA equipment of some samples containing CNT. I have plotted the storage modulus and loss modulus against temperature. But now I would like to compare these data with numerical data! Is there any possibility to simulate and obtain storage modulus as an output from any software? i.e. Abaqus, Ansys digimat etc.
I have come to a conclusion that is not possible, however, I would like to be 100% sure. Also is there any theoretical modelling to predict this viscoelastic modulus?
Dear Sebastian Tamayo, if the manufacturer of your DMA equipment is TA Instruments, they have "Advantage/Universal Analysis (UA) Software" it available for downloading as Software Downloads Links. In there, you can open original files and export datasheets or use the peak tools to see data values as many other nice tools from your data plot. If I am not wrong, you can also find output values or models of numerical data from standard materials and polymers in there, beyond other interest tools.
I hope it can help you. I think the download is free. Please, see to confirm: https://www.tainstruments.com/support/software-downloads-support/downloads/
Dear Anna,
This is very helpful, thank you. I will check out the information shared.
ANNA PAULA IS CORRECT, YOU CAN EXPORT NUMERICAL DAT FROM TA UNIVERSAL ANALYSIS AS ASCCI FILE AND THEN OPEN IT USING EXCELL OR ORIGIN.