I have modified nanoparticles then calculated the surface coverage by CC, but I got the value of Qads (adsorption reaction at electrode surface) as the negative charge. What is the effect of the negative intercept of Qads?
Article Oxidation of metal nanoparticles: Experiment and model
The charge transferred Q is calculated by integrating ∫Idt over the time interval from t1 (start) to t2(end), where the current might be as positive, as negative. You will get a negative Q if the current is negative.
Thank you very much for your kind to answer. I think to countenance with your answer. However, I have been tried to test the reaction by cyclic voltammetry then I got the positive current peak so does it relate to Q negative? Becouse I want to use the equation of Anson, 1964.
I think You will not get a negative Q if the current is positive
Hi! Can you give me a detailed description of the experimental protocol you are using both for chronocoulometric as for voltammetric measurements?
Thank you.
Maybe you used the experimental setting (working electrode, same electrolyte et al.) repeatedly, that will induce something collected on the working electrode. So it is better for you to try it again and using all the fresh setting.