I have X-Ray diffraction pattern of rGO . Can any one analysis the pattern?

More Shahid Khan's questions See All

I have use thiurea while in paper they reported urea is it the same thing ?

plz any one help me. i have some problem in my synthesis. im using th urea insted of urea which is reported in the paper is it the same thing?

03 April 2019 8,577 4 View

How to deposited CoMnO3 nano particles on FTO glass. with one step hydro thermal method?

I want to fabricate CoMnO3 nano particles through one step hydro thermal method. i kept the FTO inside the atocalve but the nano particles have very low adhesion with FTO glass what should i do...

01 February 2019 2,451 3 View

I need JCPDS file of LSFCO nanomaterial. Can anyone provide me?

Require for Rietveld refinement in XRD.

08 August 2024 3,081 2 View

How to understand this crystallographic phenomenon of low temperature crystals in zeolite?

During low-temperature testing, new diffraction peaks that appear could be indicative of several phenomena. In one of our tests, we observed notable new peaks around 40° and 45° in a specific...

06 August 2024 726 3 View

How to fix background error in rietveld refinement of one XRD peak using GSAS-II?

I want to refine one XRD peak of my in-situ xrd but the background is never working good which ultimately fails the refinement. How to refine and adjust the background using GSAS-II

05 August 2024 5,291 2 View

How to calculate the molar proportions of the oxides from the XRF analyses?

02 August 2024 2,565 2 View

Hello, regarding Mxene 2D titanium carbide?

I fabricated Ti3C2Tx using concentrated HF 40%, I plot an XRD as attached image below.. please let to know if I obtained it or not.

02 August 2024 6,789 4 View

Why Powder XRD is performed after cruhsing a crystal if Single Crystal XRD analysis of the same crystal has been performed already ?

What information we can get from PXRD analysis other than from SCXRD analysis of a crystal ?

30 July 2024 6,261 4 View

Can anyone guide me the best method to analyze the XRD data???

I will be doing an XRD on a sample which is powdered in natured and is a hydrogenated compound. I would like to know how we can understand the individual components and components by using the...

28 July 2024 4,548 2 View

Guidance needed for preparing the hydrogel samples for the XRD instrument?

I'm working with a hydrogel sample and I'd like to perform XRD analysis. Can anyone offer guidance on preparing the hydrogel for the XRD instrument? Specifically, I'm unsure about the best method...

20 July 2024 3,611 4 View

Can we measure the 2θ variation within a 5° range on a Bruker D2 Phasor XRD? is it compatible with diffraction angles (2θ) below 10°?

Can we measure the 2θ variation within a 5-degree range on a Bruker D2 Phaser XRD machine? I have experienced problems with diffraction angles (2θ) below 10 degrees. Is this range within the...

13 July 2024 2,615 4 View

How can i elucidate a compound using xrd?

XRD analysis

08 July 2024 977 4 View

Alan F Rawle

You need to post your plot.

Anagi M Balachandra

Yes please post your plot

Azhar Ali Haidry

Shahid Khan ,

you forgot to upload the plot or better to upload the origin file containing your plot, so that further insight can gained.

S. Kh. Estemirova

Maybe it cuvette

Shahid Khan

i have add the plot.

plot

First, what is GO?

It looks like after the treatment you have crystalline (2theta around 45) and amorphous (2theta around 25) compounds are formed, without knowing much of the chemistry it is hard to interpret. Do you have the raw data files.

yes i have.

GO = Graphene Oxide, I assume