If your material absorbs shorter than 301 nm you must use the excitation wavelengths shorter 301 nm. It may be observed the photoluminescence spectra caused by different defects. They can be situated in more longwavelength spectral region. I suggest you use excitation source with the shortest wavelength which is available at your disposal. It is possible you may observe photoluminescence caused by defects.