Dears
I want to ask about whether there is a method to reduce a cluster of irons-lanthanide complex?
The idea is to see the magnetic behavior if this cluster by changing the iron cluster multiplicity
Dear yahia
Thank you very much.. I will read it and find if it applicable on my system.
Try oxalic acid or citric or ascorbic acids.
Did you finish our paper
Best regards
The problem of oxalate with these type of clusters is the chelating effect. This clusters may be unstable under these conditions... But it still good to try it.
Dear Murad
The following article may help you
Visual Studio Code (VS Code) has become a popular choice among developers for several reasons: 1. **Free and Open Source**: VS Code is free to use and open source, making it accessible to...
07 August 2024 7,013 4 View
Roflumilast Cream Improves Signs and Symptoms of Plaque Psor...
29 July 2024 5,250 0 View
Many athletes face sudden death in football or Olympic games without know the causes or misunderstanding to prevent them
27 March 2024 6,257 1 View
Dose music therapy still benfit as adjustment management in cancer treatment
26 March 2024 6,122 3 View
Hello everyone, I am wondering if it is possible to import DWG file into Tekla Structures which contains 3D solid drawing with threads on and make it custom part component in tekla structures. I...
28 February 2024 6,879 0 View
What are appropriate scale that used in measuring lymphedema progress during and post chemotherapy management specially in Theraputic exercise
27 September 2023 3,579 0 View
what are the best therapeutic exercise for patient with osteoarthritis and how can measure its benefit outcomes
14 September 2023 5,631 2 View
Is there a scale or adopted questionnaire related to sport injury evaluation or follow up for assessment, management that can used .
01 September 2023 1,073 6 View
Give me strengths and weakness of this research paper
01 August 2023 9,259 0 View
If student is writing a research thesis at MS level.
31 December 2022 1,250 4 View
Generally, the target material is Mo, Co, Cu, Fe, Cr, etc, so on what basis should we choose this material?
31 July 2024 5,824 0 View
Difficulty with permittivitt and Magnetic Permeability Calculations Hello everyone, I have all the parameters related to the calculations of the permittivitty and magnetic permeability...
30 July 2024 5,206 1 View
Dear all: I am modifying Bismuth Tungstate with Hematite (Fe2O3), so I would like to know about how much Iron(+3) can form a solid solution in a Bismuth Oxide matrix. Best wishes Marco
29 July 2024 2,163 1 View
We assume that there is a physico-statistical meaning to the constant π other than circular geometry, but the iron guardians of the Schrödinger equation deny this. The iron guardians of the...
22 July 2024 4,285 9 View
1.The topic I am going to research is "Advanced Gray Wastewater Treatment Output from the Biological Process by Iron-assisted surface adsorption and UV/H2O2". I think this method has been used a...
08 July 2024 9,464 1 View
Hello All, I've been facing difficulty in executing geometry optimization of a sodium polyanionic phosphate (Na4Fe3P4O15) crystal in CASTEP (please find the input and output files attached). When...
07 July 2024 8,626 2 View
What will be the pressure in Iron Iron-Carbide diagram? It is at atmospheric pressure?
05 July 2024 1,891 0 View
here is scf file &CONTROL title = 'cal' calculation = 'scf' etot_conv_thr = 4e-6 forc_conv_thr = 1e-6 pseudo_dir='./' !tprnfor = .true. !tstress =...
29 June 2024 10,082 0 View
Someone advise me to use 1 to 2mm undersized pellet but it is not available. Do anyone have any experience in the field of tunnel kiln ?
28 June 2024 6,355 0 View
I am working on magnetic materials. I need to measure the iron core losss for my samples. can anyone help me with Ac magnetic propoerty measurement (Fe Core Loss) using BH analyser if possible? i...
26 June 2024 7,176 0 View