I would like to know how to determine the blocking temperature Tb of antiferromagntic thin film. By measure the exchange bias field HE on AFM/FM bilayer at various temperatures, we will get the HE as a function of temperature. Is the temperature where the HE shows up defined as Tb ? or the maximum of dHE/dT should be Tb? T
hanks!