The rocks are highly brecciated, ferrugenised and silicified.

besides other alterations fracture filling minerals are present that give variable chemical compositions.

Because of ferrugenisation staining is not taking properly

the altered/ friable nature more over ferrugenisation making it difficult get good polished thin sections

how do I solve this problem?