Dear Rehab,

usually the influences for calendar and cyclic aging models are considered seperately and then modelled. The temperature influence on the capacity is often modelled after the Arrhenius-effect: f(T) = e(-b/T)

The following two documents give a good overview and models you could use:Article Impedance change and capacity fade of lithium nickel mangane...

Article Combined cycling and calendar capacity fade modeling of a Ni...

As a starting point, you could use these models and try to fit the missing parameters with your dataset.

Kind regards,

Christian

Dear Christian,

Thank you so much for sharing these information. The documents are quite useful and have an intro about what to be done. Thank you again and wish you a good day.

Best regards,

Rehab

I suggest the method developed in the following paper:

Article Aging trajectory prediction for lithium-ion batteries via mo...