by CV you can get the integrated charge, which is proportional to the amount of electroactive material. If all your polymer is electroactive (and the film density is constant), then the integrated charged is proportional to the film thickness. Unfourtunately, you need some empirical factor that relates the charge and thickness (probably measured by ellipsometry)