I want to calculate the capacity of a proton battery (Q=Itplateau). However, my discharge curve has no plateau. Is it possible if I assume that t=overall discharge time?
Your total capacity is you can calculate C = VIt/weight = .25 V*(the current you implied)amps * 0.23h : Wh/gram (the amount of active material used) will give the capacity of your system in wh/kg by converting appropriately .
Same as me. the voltage drop is quite big. I suggest you to 1) reduce the thickness of the electrolyte. 2) while mix the electrodes material dont grind it, just hit it. My discharge curve always become like you if i grind.