In amorphous semiconductors (such as a-Silicon), optical band gap can be estimated from UV-Vis-NIR spectroscopy measurements. From absorption data, TAUC plot is drawn and optical band gap energy is estimated. It is a standard process for amorphous semiconductor materials and equipment is a simple UV-Vis spectrophotometer.