How important XRD estimated La and Lc values are as long as graphitic carbon nanostructure concern?

More Debananda Mohapatra's questions See All

Can the graphitization be considered as the primary condition to decide the electrical conductivity of carbonaceous materials (Graphene, CNT etc.)?

Is there any direct relation between the graphitization and the electrical conductivity of carbon materials considering their sp2/sp3 content? or any other possibilities? Please share your...

01 February 2019 3,300 11 View

What is the reason for current dropping in OER , LSV curve?

I tried four trials of the same Copper Phosphides sample in Alkaline medium ( 0.5M KOH) with Hg/HgO reference electrode and Pt as counter electrode. I used 0.001 V/s scan rate for first three...

10 August 2024 3,629 1 View

Adhesion strength of coating?

How can I determine a good adhesion strength range for coatings on polymer surfaces, such as DLC on polymer substrates? Is there a specific threshold for adhesion strength (from T-peel tests)...

10 August 2024 942 3 View

Do interactions between biosphere, carbon cycle, & water cycle impact global warming & interaction between atmosphere & hydrosphere?

How do interactions between the biosphere, the carbon cycle, and the water cycle impact global warming and interaction between the atmosphere and the hydrosphere?

09 August 2024 3,291 2 View

I need JCPDS file of LSFCO nanomaterial. Can anyone provide me?

Require for Rietveld refinement in XRD.

08 August 2024 3,081 2 View

Who of all of you will help TPEOM to re-originate the Earths atmosphere to it original 5 atmospheric elements/gases?

Global ‘Weather’ has stopped, as ‘aqua thermionic instituted by the ‘Global thermo atmospherics has instituted global thermodynamics of 120º C + and thus all waters are, or have boiled into a...

06 August 2024 8,716 0 View

How to understand this crystallographic phenomenon of low temperature crystals in zeolite?

During low-temperature testing, new diffraction peaks that appear could be indicative of several phenomena. In one of our tests, we observed notable new peaks around 40° and 45° in a specific...

06 August 2024 726 3 View

How to fix background error in rietveld refinement of one XRD peak using GSAS-II?

I want to refine one XRD peak of my in-situ xrd but the background is never working good which ultimately fails the refinement. How to refine and adjust the background using GSAS-II

05 August 2024 5,291 2 View

Binder for ZnO nanoparticles in graphite paste electrode?

I have been using paraffin, but the deposited ZnO still detach from electrode. What is the best binder to modify graphite paste electrode with ZnO nanoparticles?

03 August 2024 4,624 3 View

Why chloride turns into chlorine gas in a Downs cell?

I imagine the battery drives the graphite into a carbocation, then chloride is oxidized to donate the electron to the carbocation, but what pushes the lost electrons of chloride to be shared...

03 August 2024 5,384 0 View

How to calculate the molar proportions of the oxides from the XRF analyses?

02 August 2024 2,565 2 View

Victorya A. Chaika

Если частицы меньше 50 нм, то все известные способы будут давать разные результаты. Причем методы, которые отлично работают для других металлических и неорганических наноструктур, для графита работать не будут. Поскольку, чем меньше частица (5-10 нм). тем сильнее изменяется ее структура, а само изменение зависит от способа обработки графита.

Fernando Vallejos-Burgos

Very important. And together with d002 those are the main parameters which you can learn from graphite using XRD.

Debananda Mohapatra

Thank you Fernando Vallejos-Burgos