How can I remove particles from a PDMS mold?

07 July 2017 1 6K Report

I have some particles that are about 300 micrometers tall in a PDMS mold. I'd like to collect these particles from the mold. I've tried using tape, and although it works, removing the particles from the tape one by one is not really efficient. Are there any suggestions? Thank you

Karolina Papera Valente

Hi Chong In Shin,

Can you try some type of vacuum in order to remove the particles?

Are the particles on the surface of a piece of PDMS or inside of a channel? I feel that you expand a little bit more your question, I may be able to help you more.

Badges
Science topic

More Chong In Shin's questions See All

Any company that provides 2 photon polymerization printing services?

I have a micro-scale structure that I would like to make and it seems that 2PP is the only technology that's able to fabricate my structure. So I was wondering, if anybody knows of any company...

08 September 2017 2,374 0 View

error in running a model in Abaqus

Excessive rotation of nodes in node set ErrNodeExcessRotation-Step1

17 August 2021 0 0 View

error in modelling model in Abaqus

Excessive rotation of nodes in node set ErrNodeExcessRotation-Step1

17 August 2021 0 0 View

MGL tools

20 June 2021 0 0 View

i have some problem with chtMultiRegionSimpleFoam

--> FOAM FATAL ERROR: Maximum number of iterations exceeded From function Foam::scalar Foam::species::thermo::T(Foam::scalar, Foam::scalar, Foam::scalar, Foam::scalar (Foam::species::thermo::*)(Foam::scalar, Foam::scalar) const, Foam::scalar (Foam::species::thermo::*)(Foam::scalar, Foam::scalar) const, Foam::scalar (Foam::species::thermo::*)(Foam::scalar) const) const [with Thermo = Foam::hConstThermo >; Type = Foam::sensibleEnthalpy; Foam::scalar = double; Foam::species::thermo = Foam::species::thermo >, Foam::sensibleEnthalpy>] in file /home/ubuntu/OpenFOAM/OpenFOAM-4.1/src/thermophysicalModels/specie/lnInclude/thermoI.H at line 66. FOAM aborting #0 Foam::error::printStack(Foam::Ostream&) at ??:? #1 Foam::error::abort() at ??:? #2 Foam::heRhoThermo >, Foam::sensibleEnthalpy> > > >::calculate() at ??:? #3 Foam::heRhoThermo >, Foam::sensibleEnthalpy> > > >::correct() at ??:? #4 ? at ??:? #5 __libc_start_main in "/lib/x86_64-linux-gnu/libc.so.6" #6 ? at ??:?

24 March 2021 0 0 View

What's the best way to measure growth rates in House sparrow chicks from day 2 to day 10?

What's the best way to measure growth rates in House sparrow chicks from day 2 to day 10? Since, the growth curve from day 2 to 10 won't be like the "Logistic curve" it might not follow logistic...

03 March 2021 1,401 3 View

What is the production process of CaFe ferroalloys?

I looking for ferro calcium production process

03 March 2021 1,755 4 View

Resistor definition in Piezoelectric bimorph with ANSYS workbench

Hello, good day! I am trying to simulate similar bimorph piezoelectric harvester with below commands. However, the output power doesn't change with resistor value. Please help to find the reason. ET,10,CIRCU94,0 !SET UP RESISTOR R,1,100000 !RESISTANCE VALUE TYPE,10 !SET ELEMENT TYPE E,1,2 !CREATE RESISTOR BETWEEN NODES 1 AND 2 Thanks in advance Regards,

02 March 2021 0 0 View

Do you know any MR image dataset?

I would like to research on MR images (0.5T and 3T). Can you please suggest some websites that I can download dataset including both 0.5T and 3T MR images? Thank you.

02 March 2021 7,735 3 View

Which is suitable for use with Python? MySQL or SQL Server?

Which is suitable for use with Python? MySQL or SQL Server? What is your suggestion?

01 March 2021 3,422 3 View

How to remove the residual PDMS on the silicon mold?

Incompletely cross-linked pdms are difficult to remove.

01 March 2021 798 3 View