What would be the inner diameter? By the way why would you want to use graphite? Wouldn't alumina do? (provided that you are not heating very rapidly to prevent thermal shock). Because, alumina tubes of these diamentions can be readily bought at hundreds of companies. If you whish to make it out of graphite: Extruded products may be hard to find and drilling on this length sounds difficult to me.