How can I measured the sodium silicate solution (water glass) by thermal analysis TGA and DSC? Sodium Water glass solution very foaming.
I am not sure your question. what property of soldium silicate solution do you want to measure?
What are you interested in (heat capacity, phase transitions, glass transition, silicate content)?
If your concern is the foaming, i would suggesting trying different sample holders. You get really deep ones for TGA. You can also try using a hermetically sealed pan (at lower temperatures). Depends on what you want to measure!
You can try using hermetic pan but the amount of sample must be low. Otherwise sample pan could be burst.
Thank you for answers.
Hi Bronislav,
Did you manage to measure the TGA of Water glass. I would really like to use your conclusions on it.
I'm also interested to see the results of water glass. Did you manage to measure it?
I am working on a mulitdisciplinary project focused on environmental behaviour and attitudes towards protected areas and we need literature about focus groups that would be accesible and clear for...
01 January 1970 9,309 5 View
I would like to learn more about SPSS and Its application especially in regards to data analysis. Please suggest me how I can learn more about it. Thank you so much.
11 August 2024 9,101 4 View
I have reverse sequences (AB1 format), can I base on reverse DNA sequences to perform nucleotide alignment, convert nucleotides to amino acids and deposit the sequence in GenBank database?
11 August 2024 5,138 1 View
Hello, Why do i see this baseline drift when i compare my blank (black) to the sample (blue)? Any suggestions as to why this happened? Thank you!
11 August 2024 3,770 4 View
Willett, Shenoy et al. (2021) have developed a brain computer interface (BCI) that used neural signal collected from the hand area of the motor cortex (area M1) of a paralyzed patient. The...
10 August 2024 7,180 0 View
I'm currently exploring the application of Python in textile engineering, specifically in areas like data analysis, process automation, and the development of smart textiles. I'm interested in...
10 August 2024 7,429 2 View
How can I use the cif data obtained from rietveld refinement extracted via gsas2, for microstructural analysis using ETEX software?
09 August 2024 7,718 0 View
Let's say we have a standard, regular hexagonal honeycomb with a 3-arm primitive unit cell (something like the figure attached; the figure is only representative and not drawn to scale). The...
07 August 2024 1,937 1 View
A fungal strain was treated with nanoparticles. We want to do an environmental SEM analysis. So could anyone share your views on preparing the sample? Thank you.
07 August 2024 5,307 1 View
Hi, I have a question about normalizing the MTT OD values for doing the statistical analysis. So, if we have 3 different plates and we call them 3 different replicates, so, first we would...
07 August 2024 8,106 4 View
Hi! So i attempted to understand a novel protein behavior towards heat application by analyzing its secondary structure change. I subjected the protein to a thermal denaturation analysis using...
06 August 2024 1,989 3 View