To functionalize the carbon nanotube, I first mixed it in 3 m nitric acid at 60 °C for 15 min. Then I kept it in an ultrasonic bath for 2 hours. After drying, I repeated the same process using hydrogen peroxide. But But the degradation in the TGA analysis was minimal. What would be the reason. or how can i increase the binding of functional groups. Thank you