Hi,
In my FDTD simulation result of transmission intensity for IR source (12 µm) over thin film ( thickneess 4µm) at different angles, I found that the intensity is maximum when theta angle is 30.
may i know what could explain this and is there any experiment result to verify?
thanks
The model will have perfectly parallel surface on the film. You can expect strong etalon effects. With the film thickness close to the wavelength (given the index of refraction, the wavelength inside Silicon is about 3.5 um) you can expect the etalon to vary slowly with angle. Also, given the high index, the internal angle will change very slowly with external angle.
Try looking up etalon equations such as here: https://www.photonicsolutions.co.uk/upfiles/CXEtalons1.pdf
Geliş açısının iletim yoğunluğuna etkisi ince silikon filmin üzerindeki geliş açısının konumuna bağlıdır. Işık ışınlarının gelme, yansıma, kırılma durumlarına bağlı olur. İnce silikon üzerindeki herhangi bir konumu kimyasal bir durumdur ve ışık ışınları diğer ortama geçerken kimyasal değişikliğe uğrar. Teta açısının 30,60 veya 90 derece olması onun yüzey üzerindeki konumunu veya diğer ortamdaki kırılma durumunu belirtir. Işık ışınları diğer ortama geçtiği zaman ışığın yoğunluğu farklı olduğu için ortamın yoğunluğu da değişir. Meydana gelen olay kimyasal olur. Bu nedenle iletim ve diğer benzer özellikler değişir.
- Badges
- Science topic
- Similar topics
- Phytochemistry
- Extracts