Can you help me to interpret DSC peaks?

More Tb Bo's questions See All

Why silver nitrate white powder turn to brown powder in oven?

I was trying to dry silver nitrate powder in oven at 100C under vacuum. After couple of hours the color of silver nitrate powder turned from white to brown. does this mean, I have metallic silver...

25 October 2018 5,124 3 View

Why silver nitrate white powder turn to brown powder in oven?

I was trying to dry silver nitrate powder in oven at 100C under vacuum. After couple of hours the color of silver nitrate powder turned from white to brown. does this mean, I have metallic silver...

09 October 2018 4,668 3 View

Can you help me to interpret DSC peaks?

After synthesizing an organic polymer, I run it in DSC. There are two endothermic peaks one around 120C and another around 300C. Is this mean, I synthesized organic molecule instead of polymer?...

28 September 2016 3,226 3 View

I have a reaction product mixture with DMF and its completely soluble in DMF. Can you please let me know how I can separate them?

I added water into mixture. The solution turn to milky color but no precipitation happend. I ended up having my reaction product mixture with DMF and water. Can you please let me know how I can...

22 September 2016 8,442 1 View

How do I separate reaction product from the solvent?

I set up a synthesize reaction and used DMF as my solvent. After the reaction completed, I transferred solution in to a beaker and added about 90ml water into the beaker (picture attached). Water...

08 September 2016 7,490 7 View

Does anyone know how to extract NaOH salt from water soluble polymer powder?

I am trying to remove NaOH salt from a thermoset polymer powder that I synthesized. The polymer is water soluble. How can I remover the salt from the powder?

04 May 2016 4,972 4 View

• What the possible Persistent Organic Pollutants and Heavy metals present in fluorspar, sediments, and water bodies around its mining area?

Approximate concentrations are require in compared with the WHO permissible limts

11 August 2024 2,723 1 View

Adhesion strength of coating?

How can I determine a good adhesion strength range for coatings on polymer surfaces, such as DLC on polymer substrates? Is there a specific threshold for adhesion strength (from T-peel tests)...

10 August 2024 942 3 View

Basis set and input instruction to calculate HOMO and LUMO using Orca for Imidazolium based organic salts?

Hey there, As a synthetic chemist delving into theoretical calculations for my imidazolium-based organic molecules, I would greatly appreciate any guidance on the appropriate input instructions...

09 August 2024 5,444 7 View

How to increase simulation box size?

We intend to study the interaction between peptides and polymer (like PP, PE and PS) through MD simulations using Martini force fields ( Martini 2 for PP and Martini 3 for PE, PS). We have...

08 August 2024 4,842 0 View

Separation of organic acids-HPLC?

Hello What should be done to separate and identify organic acids in HPC when their RetTime is the same?Like oxalic acid with Propanoic Acid.or acids that have a very close RetTime.

07 August 2024 8,782 3 View

How to heat polymer for about 130° without oil bath ?

is there any other way to heat a polymer evenly other than oil bath if so what are those and how to use it

06 August 2024 947 1 View

People weight in Oaxaca Blinder Decomposition on R?

Hello guys! Do you have experience running a Oaxaca-Blinder decomposition on R applying person weights. How do you suggest doing it? I have a variable PERWT which gives more information on how...

04 August 2024 6,033 0 View

How to convert g/kg Humic acid dose to kg/ha?

I used humic acid at 0.044 g/kg soil in my pot experiment. But finally, I have to recommend kg/ha. Each pot's soil weight was 11 kg. What is the solution?

02 August 2024 7,186 6 View

How to improve peaks separation in HPLC?

Hi everyone, I'd like to better separate two close peaks coming from a bioconversion sample, I'm currently using a C18 KromaPhase 4,6mm Ø.I. SCHARLAU, particle size (µm): 10, pore size (Å): 100,...

30 July 2024 435 3 View

How to explain the different interaction between soluble and insoluble polymer in water?

Hello everyone, I am try to understand the differences interaction between insoluble and soluble polymers in water with metal ions and how theit charge density (of metal ions) affect the interaction.

29 July 2024 6,350 3 View

Mudassir Ahmed

You used DSC, can you please tell about the environment? was it air or in nitrogen ?

Tb Bo

I run DSC in Argon from room temperature to 550c 10C/min. I have very sharp endothermic peak around 120c and wide and shorter/wide endothermic peak around 300c. Unfortunately we don't have GPC to estimate the MW.

M. L. N. Madhu Mohan

Can you showt the DSC thermogram